LLDPE resin for stretch film, heavy-duty sacks, liners and rotomolded tanks, chosen by comonomer and melt index. Send an RFQ.
Linear low-density polyethylene has short, regular branches from a comonomer. It is tougher than LDPE at the same density, with better tear and puncture resistance, so film can be made thinner.
The comonomer (butene, hexene or octene) is the main quality difference between grades.
Typical values from each producer's data sheet; open a grade for full specifications.
| Grade | Producer | Type | MFR | Processing |
|---|---|---|---|---|
| ExxonMobil 1018 mLLDPE Resin | ExxonMobil | LLDPE | 1.0 g/10 min | Film Extrusion |
| SABIC 118WJ LLDPE Resin | SABIC | LLDPE | 1 g/10 min | Film Extrusion |
| SABIC 218WJ LLDPE Resin | SABIC | LLDPE | 2 g/10 min | Film Extrusion |
| SABIC 222WT LLDPE Resin | SABIC | LLDPE | 2 g/10 min | Film Extrusion |
| SABIC 920NT LLDPE Resin | SABIC | LLDPE | 0.85 g/10 min | Film Extrusion |
| SABIC M200024T LLDPE Resin | SABIC | LLDPE | 20 g/10 min | Injection Molding |
| SABIC M500026T LLDPE Resin | SABIC | LLDPE | 50 g/10 min | Injection Molding |
| SABIC R50035E LLDPE Resin | SABIC | LLDPE | 5 g/10 min (190 °C / 2.16 kg) | Rotomolding |
| Sinopec R546U LLDPE Resin | Sinopec | LLDPE | 5.05 g/10 min | Rotomolding |
No drying needed. LLDPE has a higher melt viscosity than LDPE at the same MI, so extruders run at higher pressure; blending 10–30% LDPE improves bubble stability.
General guidance only; follow the producer's TDS for each grade.