Polyphenylene oxide (PPO) is one of the world's five general-purpose engineering plastics. It has the advantages of high rigidity, high heat resistance, flame retardant, high strength and excellent electrical properties. PPO is suitable for the production of office equipment, household appliances, computer cases, chassis and precision parts.
1. The dielectric constant and dielectric loss tangent of PPO are the lowest among the five general-purpose engineering plastics, that is, the insulation function is good and the heat resistance is good. They are suitable for use in the electrical industry. It is suitable for making electrical insulating parts under wet load conditions, such as coil bobbins, tube sockets, control shafts, transformer shielding sleeves, relay boxes, insulating columns, etc.
2. PPO has excellent water resistance and hot water resistance. It is suitable for bobbins used in cooking water meters, water pumps, textile mills, etc. and durable consumer goods. The PPO plastic bobbin has a long service life.
3. PPO1 plastics are widely used in the automotive industry, such as instrument panels, protection bars, PPO and PA alloys, especially standard types with high impact resistance, and are quickly used in exterior decorative parts.
4. It can be used to make corrosion-resistant equipment. It has the advantages of light weight, chemical stability, no corrosion, good impact resistance, good transparency and wear resistance, good insulation, low thermal conductivity, good formability, good coloring, and low processing cost.
5. Regarding medical equipment, it can replace stainless steel (stainless acid-resistant steel) and other metals in the mixing filling valve of the hot water tank and exhaust fan.
Physical Properties |
Metric |
English |
Specific Gravity |
1.06 g/cc |
1.06 g/cc |
Melt Flow |
15 g/10 min |
15 g/10 min |
Mechanical Properties |
Metric |
English |
Hardness, Shore A |
87 |
87 |
Tensile Strength at Break |
18.0 MPa |
2610 psi |
|
18.0 MPa |
2610 psi |
|
27.0 MPa |
3920 psi |
|
30.0 MPa |
4350 psi |
Elongation at Break |
130 % |
130 % |
|
140 % |
140 % |
|
200 % |
200 % |
|
280 % |
280 % |
Flexural Modulus |
0.100 GPa |
14.5 ksi |
|
0.100 GPa |
14.5 ksi |
Heat Distortion |
20 % |
20 % |
Electrical Properties |
Metric |
English |
Volume Resistivity |
2.40e+16 ohm-cm |
2.40e+16 ohm-cm |
Dielectric Constant |
2.6 |
2.6 |
Dielectric Strength |
28.0 kV/mm |
711 kV/in |
Dissipation Factor |
0.0028 |
0.0028 |
Comparative Tracking Index |
600 V |
600 V |