Compared with pure PA66, the mechanical properties of glass fiber reinforced PA66 have been greatly improved, making glass fiber reinforced PA66 widely used in the automotive industry.
Features and applications: The heat distortion temperature is increased from 70°C to over 220°C, and the aging resistance is significantly improved. It can be safely used in automobile, machinery, chemical industry and other fields to manufacture heat-resistant and stressed structural parts, such as automotive pressure regulating tank, air intake manifold, throttle body radiator groove, fan blade guard and other parts.
The shrinkage of PA66 mold filled with glass fiber is reduced, making PA66 products flat and free of warping, and the size is more stable. It is widely used in precision parts such as gears and coil frames.
The corrosion resistance of glass fiber reinforced PA66 has also been significantly improved, which can meet the requirements of automotive radiator tanks, brackets in the middle of radiators, water inlet pipes, oil pans, oil-filled tanks, oil levels, and automotive water chambers.
Compared with ordinary PA66, the mechanical strength, rigidity, heat resistance, creep resistance and fatigue resistance of glass fiber reinforced PA66 are greatly improved, while the elongation, molding shrinkage and hygroscopicity are reduced.
In summary, glass fiber reinforced PA66 has high specific strength, good heat resistance, electrical properties, abrasion resistance, high impact resistance, simple processing method, low production cost, high efficiency, economical and environmental protection, etc. characteristic. It expands the application space of PA66 products in automobiles and electronic appliances, and is also widely used in high-end mechanical parts, shields, fan blades, automotive cooling water tanks, gears, coil bobbins, toothed belt covers, chain guides, and window heat insulation profiles. application field.
performance item |
Test Conditions |
testing method |
value/description |
unit |
|
Mechanical behavior |
Tensile strength (tensile strength) |
|
ASTM D638/ISO 527 |
130(broken) |
kg/cm2(MPa)[Lb/in2] |
elongation at break |
|
ASTM D638/ISO 527 |
3.5 |
% |
|
Tensile modulus |
|
ASTM D638/ISO 527 |
7500 |
kg/cm2(MPa)[Lb/in2] |
|
Bending strength |
|
ASTM D790/ISO 178 |
|
kg·cm/cm(J/M)ft·lb/in |
|
Rockwell hardness |
|
ASTM D785 |
|
|
|
Physical properties |
specific gravity (density) |
|
ASTM D792/ISO 1183 |
1.45 |
|
Molding shrinkage |
|
ASTM D955 |
0.6~1.1 |
% |
|
Melt Index (Flow Coefficient) |
200℃/5kg |
ASTM D1238/ISO 1133 |
|
g/10min |
|
220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
||
Water absorption 23℃/24H |
|
ASTM D570/ISO 62 |
1.4 |
% |
Application range: