Description
Marlex HXM50100 is an HDPE grade. Processing method: Blow Molding.
Applications
Primary processing method: Blow Molding.
Product Specification
| NOMINAL PHYSICAL PROPERTIES | English | SI | Method |
|---|---|---|---|
| Density | – | 0.948 g/cm³ | ASTM D1505 |
| Flow Rate (HLMI, 190 °C/21.6 kg) | – | 10.0 g/10 min | ASTM D1238 |
| Tensile Strength at Yield, 2 in/min, Type IV bar | 3,600 psi | 25 MPa | ASTM D638 |
| Elongation at Break, 2 in/min, Type IV bar | 700 % | 700 % | ASTM D638 |
| Flexural Modulus, Tangent – 16:1 span:depth, 0.5 in/min | 175,000 psi | 1,200 MPa | ASTM D790 |
| ESCR, Condition B (100 % Igepal), F50 | > 1,000 h | > 1,000 h | ASTM D1693 |
| Durometer Hardness, Type D (Shore D) | 68 | 68 | ASTM D2240 |
| Vicat Softening Temperature, Loading 1, Rate A | 258 °F | 126 °C | ASTM D1525 |
| Heat Deflection Temperature, 66 psi, Method A | 173 °F | 78 °C | ASTM D648 |
| Brittleness Temperature, Type A, Type I specimen | < -103 °F | < -75 °C | ASTM D746 |
| Tensile Impact, Type S bar | 90 ft•lb/in2 | 190 kJ/m² | ASTM D1822 |
Typical values should be confirmed against the latest producer-issued TDS before final use.