Description
Marlex HHMTR-144 is an HDPE grade. Processing method: Film Extrusion.
Applications
Primary processing method: Film Extrusion.
Product Specification
| Nominal Resin Properties | Value (SI Units) | Method |
|---|---|---|
| Density | 0.946 g/cm3 | ASTM D1505 |
| Melt Index, Condition 190°C / 2.16 kg | 0.18 g/10 min | ASTM D1238 |
| Brittleness Temperature, Type A clamp, Type I specimen | <-75°C | ASTM D746 |
| ESCR, Condition B (100% Igepal), F50 | >1000 hrs | ASTM D1693 |
| Flexural Modulus, Tangent – 16:1 span:depth, 12.7 mm/min | 1150 MPa | ASTM D790 |
| Dart Drop (66 cm) | 90 g | ASTM D1709 |
| Tensile Strength at Yield, 50.8 mm/min MD | 24 MPa | ASTM D882 |
| Tensile Strength at Yield, 50.8 mm/min TD | 26 MPa | ASTM D882 |
| Elongation at Break, 50.8 mm/min MD | 480% | ASTM D882 |
| Elongation at Break, 50.8 mm/min TD | 640% | ASTM D882 |
| Elmendorf Tear Strength, MD | 19 g | ASTM D1922 |
| Elmendorf Tear Strength, TD | 270 g | ASTM D1922 |
Typical values should be confirmed against the latest producer-issued TDS before final use.