Description
BJ368MO is a polypropylene copolymer with good flow and an optimum combination of high stiffness and high impact strength.
The material is nucleated with Borstar Nucleation Technology (BNT). Its flow, nucleation and stiffness can help reduce moulding cycle time. It also provides good antistatic performance and good mould-release properties.
Packaging
Heavy-duty packaging film bags, net weight 25 kg per bag.
Applications
Thin-wall containers and food-packaging applications.
Product Specification
| Properties | Typical Value | Test Method |
|---|---|---|
| Density | 905 kg/m³ | ISO 1183 |
| Melt Flow Rate (230°C/2.16 kg) | 70 g/10 min | ISO 1133 |
| Flexural Modulus | 1,400 MPa | ISO 178 |
| Tensile Modulus (50 mm/min) | 1,500 MPa | ISO 527-2 |
| Tensile Strain at Yield (50 mm/min) | 4% | ISO 527-2 |
| Tensile Stress at Yield (50 mm/min) | 25 MPa | ISO 527-2 |
| Heat Deflection Temperature | 100°C | ISO 75-2 |
| Charpy Impact Strength, notched (23°C) | 5.5 kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 5.5 kJ/m² | ISO 179/1eA |