Description
Juheshun J2700 is a PA6 Resin grade. Processing method: Fiber.
Applications
Primary processing method: Fiber.
Product Specification
| Property | Test Method | Test Conditions | Unit | Test Result |
|---|---|---|---|---|
| Grade | J2700 | |||
| Specification | ||||
| Relative Viscosity (RV) | ISO 307 | Requirement: 2.70±0.05 | – | 2.70 |
| Viscosity Number (VN) | ISO 307 | / | – | 149.88 |
| Hot-water Extractable Content | ISO 6427 | Requirement: ≤0.50 | % | 0.30 |
| Moisture Content | ISO 15512 | Requirement: ≤0.06 | % | 0.04 |
| Melting Point | ISO 11357 | / | ℃ | 220.98 |
| Mechanical Properties | ||||
| Tensile Strength | ISO 527 | 20mm/min | MPa | 68.5 |
| Tensile Elongation at Break | ISO 527 | 20mm/min | % | 32.5 |
| Bending Strength | ISO 178 | 5mm/min | MPa | 89.33 |
| Bending Modulus | ISO 178 | 5mm/min | MPa | 2019.02 |
| Cantilever Beam Notch Impact Strength | ISO 180 | 2.75J | kJ/m² | 8.16 |
| Impact Strength of Simply Supported Beam Gap | ISO 179 | 4J | kJ/m² | 8.28 |
| Impact Strength of Simply Supported Beam Without Notch | ISO 179 | 4J | kJ/m² | Not broken |
| Thermal / Flow Properties | ||||
| Hot Deformation Temperature | ISO 75-2 | 1.82MPa | ℃ | 62.80 |
| Melt Index | ISO 1133 | 230℃, 2160g | g/10min | 22.26 |
| Other Properties | ||||
| Shore Hardness | ISO 868 | HD | – | 78.00 |
Typical values should be confirmed against the latest producer-issued TDS before final use.