Description
DOW XZ-89609 is an HDPE grade. Processing method: Injection Molding.
Applications
Primary processing method: Injection Molding.
Product Specification
| PROPERTIES | Nominal Value (English) | Nominal Value (SI) | TEST METHODS |
|---|---|---|---|
| Denslity | 0.963 g/cm³ | 0.963 g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (190℃/2.16 kg) | 8.0 g/10 min | 8.0 g/10 min | ISO 1133 |
| Environmentall Stress-Cracking Resistance(ESCR) 10% Igepal, Compression Molded | 3.00 hr | 3.00 hr | ASTM D1693 |
| Tensille Strength（Yield, Compression Molided） | 4210 psi | 29.0 MPa | ISO 527-2 |
| Tensille Strength（Break, Compression Molded） | 3190 psl | 22.0 MPa | ISO 527-2 |
| Tensille Elongation（Break, Compression Molded） | 1200 % | 1200 % | ISO 527-2 |
| Flexural Modulus – 2% Secant (Compression Molided) | > 145000 psi | > 1000 MPa | ISO 527-2 |
| Charpy Notched Impact Strength2 Compression Molded | 3.0 ft-lb/in² | 6.3 kJ/m² | ISO 179/1eA |
| Shore Hardness (Shore D, Compression Molded) | 66 | 66 | ASTM D2240 |
| Vicat Softening Temperature | 264 °F | 129 °C | ASTM D1525 |
Typical values should be confirmed against the latest producer-issued TDS before final use.