Description
Yuhwa RP2400 is a polypropylene grade. Product type: Random Copolymer. Processing method: Pipe Extrusion.
Packaging
In 25kg bag, 28mt in one 40HQ without pallet.
Applications
Primary processing method: Pipe Extrusion.
Product Specification
| Item | Value | Unit | Method |
|---|---|---|---|
| Melt Index | 0.25 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm³ | ASTM D1505 |
| Tensile Strength at Yield | 230 | kgf /cm2 | ASTM D638 |
| Elongation at Break | >600 | % | ASTM D638 |
| Flexural Modulus | 8500 | kgf /cm2 | ASTM D790 |
| Hardness (Rockwell) | 72 | R Scale | ASTM D785 |
| Impact Strength (Izod with Notch) | NB | kgf cm/cm | ASTM D256 |
| Melting Point | 139 | ℃ | ASTM D3418 |
| Softening Point (Vicat) | 133 | ℃ | ASTM D1525 |
| Oxidation Induction Time at 200°C | >30 | min | ASTM D3895 |
| Heat Deflection Temperature | 85 | ℃ | ASTM D648 |
| Ash Contents | <300 | ppm | ASTM D5630 |
| Minimum Required Strength | 11.2 | MPa | ISO 9080 |
Typical values should be confirmed against the latest producer-issued TDS before final use.