Description
Borouge BE961MO is a polypropylene grade. Product type: Impact Copolymer. Processing method: Injection Molding.
Packaging
Heavy-duty packaging film bags, net weight 25kg per bag
Applications
Primary processing method: Injection Molding.
Product Specification
| Properties | Typical Value | Test Method |
|---|---|---|
| Density | 900-910kg/m³ | ISO 1183 |
| Melt Flow Rate(230°C/2.16kg) | 12g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1200MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 5.3% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 23MPa | ISO 527-2 |
| Flexural Modulus | 1250MPa | ISO 178 |
| Tensile Strain at Yield | 5.3% | ASTM D638 |
| Tensile Stress at Yield | 23MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1200MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 14kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 7kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 160J/m | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 75J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa) | 92°C | ISO 75-2 |
| Vicat Softening Temperature(Method A) | 144°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 87 | ISO 2039-2 |
Typical values should be confirmed against the latest producer-issued TDS before final use.