Description
Lihuayi Weiyuan WY-111BR is a PC Resin grade. Processing method: Injection Molding.
Applications
Primary processing method: Injection Molding.
Product Specification
| Property | Unit | Test Condition | Result | Test Method | ||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Melt Mass-Flow Rate | g/10min | 300℃,1.2 Kg | 11 | ASTM D1238 | ||||||||||||||||||||
| Haze | % | 3.2mm | 0.4 | ASTM D1003 | ||||||||||||||||||||
| Transmittance | % | 3.2mm | 90 | ASTM D1003 | ||||||||||||||||||||
| Mass Density | / | 23℃ | 1.2 | ASTM D792 | ||||||||||||||||||||
| Hardness | L | / | 99.6 | ASTM D785 | ||||||||||||||||||||
| Tensile Strength | Kg/cm 2 | 6 mm/min(Yield) | 637 | ASTM D638 | ||||||||||||||||||||
| Tensile Elongation | % | 6 mm/min | 100 | ASTM D638 | ||||||||||||||||||||
| Flexural Strength | MPa | 1.3 mm/min | 99.5 | ASTM D790 | ||||||||||||||||||||
| Flexural Modulus | 100000 Kg/cm 2 | 1.3 mm/min | 2.45 | ASTM D790 | ||||||||||||||||||||
| Izod Impact Strength | Kg-cm/cm | 3.2 mm, 23℃ | 85 | ASTM D256(Notched) | ||||||||||||||||||||
| Vicat Softening Temp | ℃ | 1 Kg,120 ℃/hr | 155 | ASTM D1525 | ||||||||||||||||||||
| Heat Distortion Temp | ℃ | 132℃×8 hours Loading 4.6 kg/cm 2 | 146 | ASTM D648(Annealed) | ||||||||||||||||||||
| UL Flammability | / | / | V-0 | UL 94 | ||||||||||||||||||||
| Formed shrinkage | % | Parallel Direction | 0.8 | ISO 294-4 | ||||||||||||||||||||
Typical values should be confirmed against the latest producer-issued TDS before final use.