Flame retardant PPO plastic Polymer A0501

Product Item : 924
Category： PPO Resin
INQUIRY EMAIL

PPO is a kind of high temperature resistant thermoplastic resin. Polyphenylene ether (PPO/PPE) is a thermal engineering plastic with high temperature resistance, which has excellent acid resistance, alkali resistance and chemical reagent resistance. The chemical name of polyphenylene ether is poly 2,6-di-1,4-benzene Ether, referred to as PPO or PPE. Also known as polyphenylene ether (PPO/PPE), it is a thermal engineering plastic resistant to higher temperatures, with excellent acid resistance, alkali resistance, and chemical reagent resistance. The chemical name of polyphenylene ether is poly 2,6-di-1 4-Phenyl ether, commonly used in the market is mainly modified polyphenylene ether, referred to as MPPO or MPPE.

PPO application:

Electronic appliances: It can meet the requirements of excellent point insulation under the conditions of humidity, load and high temperature. It is used to prepare TV tuners, coil cores, microwave insulation parts, shielding sleeves, and high-frequency printed circuit boards. All kinds of high-voltage electronic components, TV sets, computers, fax machines, repeater shells, etc.

Automotive industry: suitable for instrument panel parts, window frames, shock absorbers, pump filters, etc.

Machinery industry: used as gears, bearings, pump impellers, blower impellers, etc.

Chemical industry: used to make corrosion-resistant parts such as pipelines, valves, filters and submersible pumps.

Physical Properties	Metric	English
Specific Gravity	1.11 g/cc	1.11 g/cc
Moisture Absorption	0.400 %	0.400 %
Linear Mold Shrinkage	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in
Mechanical Properties	Metric	English
Tensile Strength, Yield	58.0 MPa	8410 psi
Elongation at Break	55 %	55 %
Flexural Strength	78.0 MPa	11300 psi
Flexural Modulus	2.23 GPa	323 ksi
Izod Impact, Notched	1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C	2.75 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F
Thermal Properties	Metric	English
CTE, linear	100 µm/m-°C @Temperature -30.0 - 60.0 °C	55.6 µin/in-°F @Temperature -22.0 - 140 °F
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Processing Properties	Metric	English
Processing Temperature	250 - 280 °C	482 - 536 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	100 - 110 °C	212 - 230 °F
Dry Time	3 - 4 hour	3 - 4 hour