Description
Borouge RH668MO is a polypropylene grade. Product type: Random Copolymer. Processing method: Injection Molding.
Packaging
Heavy-duty packaging film bags, net weight 25kg per bag
Applications
Primary processing method: Injection Molding.
Product Specification
| Property | Typical Value | Test Method |
|---|---|---|
| Density | 900-910kg/m3 | ISO 1183 |
| Melt Flow Rate(230°C/2.16kg) | 40g/10min | ISO 1133 |
| Tensile Modulus (1 mm/min) | 1050MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 12% | ISO 527-2 |
| Tensile Stress at Yield (50 mm/min) | 28MPa | ISO 527-2 |
| Flexural Modulus | 1050MPa | ISO 178 |
| Flexural Modulus(by 1% se canf) | 1000MPa | ASTM D790A |
| Charpy Impact Strength, notched (23C) | 6kJ/m² | ISO 179/1 eA |
| IZOD Impact Strength, notched (23℃) | 55J/m | ASTM D256 |
| Heat Deflection Temperature (0,45 N/mm²) | 70°C | ISO 75-2 |
| Vicat Softening Temperature(Method A) | 120.0C | ISO 306 |
| Haze(2mm) | 16% | ASTM D1003 |
| Hardness, Rockwell(R-scale) | 90 | ISO 2039-2 |
Typical values should be confirmed against the latest producer-issued TDS before final use.