Description
Kingfa T30H is a polypropylene grade. Product type: Homopolymer. Processing method: Extrusion.
Packaging
In 25kg bag, 28mt in one 40HQ without pallet.
Applications
Primary processing method: Extrusion.
Product Specification
| properties | Test Standard | Test Condition | S.I. Unit | S.I. Typical Value |
|---|---|---|---|---|
| Mechanical | ||||
| Tensile Strength | ISO 527-2 | 50mm/min | MPa | 34 |
| Tensile Strain at Break | ISO 527-2 | 50mm/min | % | 50 |
| Flexural Strength | ISO 178 | 2mm/min | MPa | 38 |
| Flexural Modulus | ISO 178 | 2mm/min | MPa | 1350 |
| Izod Notched Impact Strength | ISO 180 | 4mm, 23℃ | KJ/m2 | 4 |
| Thermal | ||||
| Temperature of Deflection Under Load | ISO 75-2 | 0.45MPa | ℃ | 105 |
| Electrical | ||||
| Volume Resistivity | IEC 60093 | — | Ω ·cm | 1016 |
| Others | ||||
| Density | ISO 1183- 1 | 23℃ | g/cm3 | 0.9 |
| Melt Mass-flow Rate(MFR) | ISO 1133- 1 | 230℃, 2.16kg | g/10min | 4.5 |
| Molding Shrinkage | KINGFA | — | % | 1.4- 1.8 |
| Flammability | UL 94 | 1.5mm | Class | HB |
| 3.0mm | Class | HB | ||
Typical values should be confirmed against the latest producer-issued TDS before final use.