Antistatic masterbatch is a functional plastic product additive specially developed for non-polar plastic product polymer materials; due to the poor water absorption of non-polar plastic product polymer materials, when plastic products rub against each other Finally, the accumulated charges will be difficult to diffuse and release on the surface of the plastic product, making the electrostatic properties of the plastic product larger and stronger. At this time, if the charge accumulated on the surface of the plastic product is not evacuated in time, it will cause the operator of the plastic product to be exposed to electric waves during the manufacturing process. During the manufacturing process of plastic bags and when packaging goods, the charge accumulated on the surface of the product will make the film adhere to the packaging equipment or other objects, which greatly reduces the production efficiency. Or during the sales process, a large amount of dust will be adsorbed on the surface of the plastic product, which will seriously affect the appearance of the plastic product.
Antistatic masterbatch features:
It can effectively avoid the static electricity generated due to the insulating properties of the high polymer itself so that it can adapt quickly; it has good compatibility with the product resin; the antistatic effect is long-lasting; it has good optical properties, low haze, and high gloss at the same time Its dispersibility and weather resistance are excellent.
Product Usage:
Anti-static masterbatches are now widely used in injection molding, blow molding, blister, coating, coating, lamination, blown film, cast film, stretch film, packaging film, flat bag, vest bag, bubble bag, plastic Sheet and other products and industries.
Physical Properties |
Metric |
English |
Comments |
Density |
0.918 g/cc |
0.0332 lb/in³ |
ASTM D792 |
Thickness |
38.1 microns |
1.50 mil |
|
Melt Flow |
2.0 g/10 min |
2.0 g/10 min |
ASTM D1238 |
|
|||
Mechanical Properties |
Metric |
English |
Comments |
Film Tensile Strength at Yield, MD |
10.0 MPa |
1450 psi |
ASTM D882 |
Film Tensile Strength at Yield, TD |
9.00 MPa |
1310 psi |
ASTM D882 |
Film Elongation at Break, MD |
690 % |
690 % |
ASTM D882 |
Film Elongation at Break, TD |
740 % |
740 % |
ASTM D882 |
Secant Modulus, MD |
0.180 GPa |
26.1 ksi |
ASTM D882 |
Secant Modulus, TD |
0.200 GPa |
29.0 ksi |
ASTM D882 |
Coefficient of Friction |
>= 0.70 |
>= 0.70 |
ASTM D1894 |
Elmendorf Tear Strength, MD |
3.50 g/micron |
88.9 g/mil |
ASTM D1922 |
Elmendorf Tear Strength, TD |
10.6 g/micron |
269 g/mil |
ASTM D1922 |
Dart Drop |
3.00 g/micron |
76.2 g/mil |
F 50; ASTM D1709/A |
Film Tensile Strength at Break, MD |
30.0 MPa |
4350 psi |
ASTM D882 |
Film Tensile Strength at Break, TD |
25.0 MPa |
3630 psi |
|
Application range: