Description
DuPont 101L is a PA66 Resin grade.
Product Specification
| Property | Test Method | Test Conditions | Unit | Test Result |
|---|---|---|---|---|
| Grade | Zytel® 101L NC010 | |||
| General Information | ||||
| Resin Identification | ISO 1043 | / | – | PA66 |
| Part Marking Code | ISO 11469 | / | – | PA66 |
| Rheological Properties | ||||
| Viscosity Number | ISO 307, 1157, 1628 | Sulfuric Acid 96% | cm³/g | 150 |
| Moulding Shrinkage, Parallel | ISO 294-4, 2577 | Dry | % | 1.4 |
| Moulding Shrinkage, Normal | ISO 294-4, 2577 | Dry | % | 1.4 |
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527-1/-2 | Dry / Conditioned | MPa | 3100 / 1400 |
| Yield Stress | ISO 527-1/-2 | Dry / Conditioned | MPa | 82 / 55 |
| Yield Strain | ISO 527-1/-2 | Dry / Conditioned | % | 4.5 / 25 |
| Nominal Strain at Break | ISO 527-1/-2 | Dry / Conditioned | % | 25 / >50 |
| Strain at Break | ISO 527-1/-2 | 23℃, 50mm/min | % | 45 |
| Flexural Modulus | ISO 178 | Dry / Conditioned | MPa | 2800 / 1200 |
| Charpy Notched Impact Strength | ISO 179/1eA | 23℃, Dry / Conditioned | kJ/m² | 5.5 / 15 |
| Izod Notched Impact Strength | ISO 180/1A | 23℃, Dry / Conditioned | kJ/m² | 5.5 / 12 |
| Ball Indentation Hardness | ISO 2039-1 | H 358/30, Dry / Conditioned | MPa | 180 / 85 |
| Rockwell Hardness, M-Scale | ISO 2039-2 | Dry / Conditioned | – | 79 / 59 |
| Rockwell Hardness, R-Scale | ISO 2039-2 | Dry / Conditioned | – | 121 / 108 |
| Thermal Properties | ||||
| Melting Temperature | ISO 11357-1/-3 | 10℃/min, Dry | ℃ | 262 |
| Glass Transition Temperature | ISO 11357-1/-2 | 10℃/min, Dry | ℃ | 60 |
| Heat Deflection Temperature | ISO 75-1/-2 | 1.8MPa | ℃ | 70 |
| Heat Deflection Temperature | ISO 75-1/-2 | 0.45MPa | ℃ | 190 |
| Vicat Softening Temperature | ISO 306 | 50℃/h, 50N | ℃ | 240 |
| Coefficient of Linear Thermal Expansion, Parallel | ISO 11359-1/-2 | Dry | E-6/K | 100 |
| Coefficient of Linear Thermal Expansion, Normal | ISO 11359-1/-2 | Dry | E-6/K | 110 |
| Flammability | ||||
| Burning Behavior | IEC 60695-11-10 / UL 94 | 1.5mm nominal thickness | Class | V-2 |
| Oxygen Index | ISO 4589-1/-2 | Dry | % | 28 |
| Glow Wire Flammability Index | IEC 60695-2-12 | 0.75mm / 1.5mm / 3mm | ℃ | 960 / 960 / 960 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | 0.75mm / 1.5mm / 3mm | ℃ | 725 / 750 / 800 |
| Electrical Properties | ||||
| Relative Permittivity | IEC 62631-2-1 | 100Hz, Dry / Conditioned | – | 3.8 / 11 |
| Relative Permittivity | IEC 62631-2-1 | 1MHz, Dry / Conditioned | – | 3.5 / 4 |
| Volume Resistivity | IEC 62631-3-1 | Dry / Conditioned | Ω·m | 1E12 / 1E10 |
| Electric Strength | IEC 60243-1 | Dry / Conditioned | kV/mm | 32 / 28 |
| Comparative Tracking Index | IEC 60112 | Dry | – | 600 |
| Other Properties | ||||
| Density | ISO 1183 | Dry | kg/m³ | 1140 |
| Humidity Absorption | Sim. to ISO 62 | 2mm | % | 2.6 |
| Water Absorption | Sim. to ISO 62 | 2mm | % | 8.5 |
| Water Absorption, Immersion | Sim. to ISO 62 | 24h, 1mm thickness | % | 4.2 |
| Injection Molding Conditions | ||||
| Drying Recommended | / | Injection Moulding | – | Yes |
| Drying Temperature | / | Dehumidified Dryer | ℃ | ≥80 |
| Drying Time | / | Dehumidified Dryer | h | 2–4 |
| Processing Moisture Content | / | Before Processing | % | ≤0.2 |
| Melt Temperature | / | Optimum | ℃ | 290 |
| Melt Temperature Range | / | Minimum / Maximum | ℃ | 280–300 |
| Mold Temperature | / | Optimum | ℃ | 70 |
| Mold Temperature Range | / | Minimum / Maximum | ℃ | 50–90 |
| Hold Pressure Range | / | Injection Moulding | MPa | 50–100 |
| Hold Pressure Time | / | Injection Moulding | s/mm | 4 |
Typical values should be confirmed against the latest producer-issued TDS before final use.