Description
Borouge BF970MO is a polypropylene grade. Product type: Impact Copolymer. Processing method: Injection Molding.
Packaging
Heavy-duty packaging film bags, net weight 25kg per bag
Applications
Primary processing method: Injection Molding.
Product Specification
| Properties | Typical Value | Test Method |
|---|---|---|
| Density | 900-910kg/m³ | ISO 1183 |
| Melt Flow Rate(230°C/2.16kg) | 20g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1500MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 5% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 27MPa | ISO 527-2 |
| Flexural Modulus | 1450MPa | ISO 178 |
| Tensile Strain at Yield | 5% | ASTM D638 |
| Tensile Stress at Yield | 27MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1400MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 9kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 4,5kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 95J/m | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 55J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa) | 102°C | ISO 75-2 |
| Vicat Softening Temperature(Method A) | 149°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 92 | ISO 2039-2 |
Typical values should be confirmed against the latest producer-issued TDS before final use.